物性纠错
| 熔体体积流动速率 | 300°C/1.2kg | ISO1133 | 10.0 | cm3/10min |
| 收缩率 | ISO294-4 | 0.50to0.70 | % | |
| 密度 / 比重2 | ASTMD792 | 1.20 | g/cm³ | |
| 密度 / 比重 | 23°C | ISO1183 | 1.20 | g/cm³ |
| 熔体质量流动速率 | 300°C/1.2kg | ASTMD1238 | 10 | g/10min |
| 弯曲应力5 | ISO178 | 90.0 | Mpa | |
| 抗张强度3 | 屈服 | ASTMD638 | 61.6 | Mpa |
| 拉伸应力 | 屈服 | ISO527-2/50 | 65.0 | Mpa |
| 断裂 | ISO527-2/50 | 75.0 | Mpa | |
| 伸长率4 | 断裂 | ASTMD638 | 110 | % |
| 拉伸应变 | 断裂 | ISO527-2/50 | 120 | % |
| 弯曲模量4 | ASTMD790 | 2340 | Mpa | |
| 弯曲模量5 | ISO178 | 2400 | Mpa | |
| 弯曲强度4 | ASTMD790 | 89.8 | Mpa | |
| 线形热膨胀系数 | MD | ISO11359-2 | 6.0E-5to8.0E-5 | cm/cm/°C |
| 热变形温度6 | 0.45MPa,Annealed | ASTMD648 | 145 | °C |
| 热变形温度 | 1.8MPa,未退火 | ISO75-2/A | 127 | °C |
| 1.8MPa,退火 | ISO75-2/A | 142 | °C | |
| 维卡软化温度 | -- | ISO306/A50 | 148 | °C |
| -- | ISO306/B50 | 143 | °C | |
| 简支梁缺口冲击强度 | 23°C | ISO179 | 75 | kJ/m² |
| 悬壁梁缺口冲击强度 | 23°C,3.20mm | ASTMD256 | 850 | J/m |
| 23°C | ISO180/4A | 75 | kJ/m² | |
| 洛氏硬度 | M级 | ASTMD785 | 77 | |
| UL阻燃等级 | 1.5mm | UL94 | V-2 |