| 密度 / 比重 | ASTM D792 | 1.19 | ||
| 收缩率 | % | 0.6-0.8 | ||
| 熔融指数 | g/10min | ASTM D1238 | 10 | |
| 屈服拉伸强度 | 50mm/min | kgf/cm | ASTM D638 | |
| 断裂拉伸强度 | 50mm/min | kgf/cm | ASTM D638 | 660 |
| 屈服拉伸应变 | 50mm/min | % | ASTM D638 | |
| 断裂拉伸应变 | 50mm/min | % | ASTM D638 | |
| 拉伸模量 | 50mm/min | kgf/cm | ASTM D638 | 23200 |
| 弯曲应力 | kgf/cm | ASTM D790 | 1030 | |
| 弯曲模量 | kgf/cm | ASTM D790 | 23900 | |
| IZOD缺口冲击强度 | 23℃ | ASTM D256 | 81 | |
| 维卡软化温度 | ℃ | ASTM D1525 | ||
| 热变形温度 | -，0.45 | ℃ | ASTM D648 | |
| -，1.82Mpa | ℃ | ASTM D648 | 126 |