| 比重 | 1.19 | g/cm3 | ASTM D792 |
| 表观密度 | 0.66 | g/cm3 | ASTM D1895 |
| 熔流率(熔体流动速率) (230°C/3.8 kg) | 3.3 | g/10 min | ASTM D1238 |
| 收缩率 - 流动 | 0.40 到 0.70 | % | ASTM D955 |
| 吸水率 (平衡) | < 0.30 | % | ASTM D570 |
| 洛氏硬度 (M 级) | 95 | ASTM D785 |
| 拉伸模量 | 3240 | MPa | ASTM D638 |
| 抗张强度 | 77.9 | MPa | ASTM D638 |
| 伸长率 | ASTM D638 | ||
| 屈服 | 4.0 到 6.0 | % | ASTM D638 |
| 断裂 | 4.0 到 6.0 | % | ASTM D638 |
| 弯曲模量 | 3450 | MPa | ASTM D790 |
| 弯曲强度 | 112 | MPa |