物性纠错
| 密度 | ASTM D792/ISO 1183 | 1.18 | ||
| 成型收缩率 | ASTM D955 | 0.4-0.7 | % | |
| 熔融指数（流动系数） | ASTM D1238/ISO 1133 | 24 | g/10min | |
| 吸水率 23℃/24H | ASTM D570/ISO 62 | 0.3 | % | |
| 断裂伸长率 | ASTM D638/ISO 527 | 12 | % | |
| 拉伸强度 | ASTM D638/ISO 527 | 57 | kg/cm²(MPa)[Lb/in²] | |
| 洛氏硬度 | ASTM D785 | 80 | ||
| 弯曲模量 | ASTM D790/ISO 178 | 2600 | kg/cm²(MPa)[Lb/in²] | |
| 弯曲强度 | ASTM D790/ISO 178 | 92 | kg/cm²(MPa)[Lb/in²] | |
| Charpy冲击强度 | ASTM D256/ISO 179 | 1.6 | kg·cm/cm(J/M)ft·lb/in | |
| 模糊系数（Haze） | ISO 14782 | 0.7 | % | |
| 透光率 | ASTM D1003/ISO 13468 | 92 | % | |
| 折射率 | ASTM D542/ISO 489 | 1.49 | ||
| 维卡软化点 | ASTM D1525/ISO R306 | 89 | ℃（℉） |