物性纠错
| 密度 | ASTM D792/ISO 1183 | 1.19 | ||
| 成型收缩率 | ASTM D955 | 0.3-0.8 | % | |
| 熔融指数（流动系数） | ASTM D1238/ISO 1133 | 1.0 | g/10min | |
| 吸水率 23℃/24H | ASTM D570/ISO 62 | 0.4 | % | |
| 断裂伸长率 | ASTM D638/ISO 527 | 720 | % | |
| 拉伸模量 | ASTM D638/ISO 527 | 600 | kg/cm²(MPa)[Lb/in²] | |
| 拉伸强度 | ASTM D638/ISO 527 | 390 | kg/cm²(MPa)[Lb/in²] | |
| 伸长率 | ASTM D638/ISO 527 | 5.9 | % | |
| 洛氏硬度 | ASTM D785 | 45 | ||
| 弯曲模量 | ASTM D790/ISO 178 | 19000 | kg/cm²(MPa)[Lb/in²] | |
| 弯曲强度 | ASTM D790/ISO 178 | 720 | kg/cm²(MPa)[Lb/in²] | |
| 拉伸断裂伸长率(延伸率) | ASTM D638/ISO 527 | 380 | % | |
| IZOD 缺口冲击强度 | ASTM D256/ISO 179 | 5.9 | kg·cm/cm(J/M)ft·lb/in | |
| ASTM D256/ISO 179 | 57.9 | kg·cm/cm(J/M)ft·lb/in | ||
| ASTM D256/ISO 179 | 7 | kg·cm/cm(J/M)ft·lb/in | ||
| ASTM D256/ISO 179 | 6 | kg·cm/cm(J/M)ft·lb/in | ||
| 透光率 | ASTM D1003/ISO 13468 | 91 | % | |
| 折射率 | ASTM D542/ISO 489 | 1.49 | ||
| 热变形温度 | ASTM D648/ISO 75 | 79 | ℃（℉） | |
| 维卡软化点 | ASTM D1525/ISO R306 | 98 | ℃（℉） |